If investment material is burned out too quickly, what will most likely occur?

When investment material is burned out too quickly, the most likely result is cracking of the investment. This occurs because rapid heating can create a sudden temperature differential within the material, leading to thermal stress. As the inner layers heat up more quickly than the outer layers, the expansion of the inner layers can cause the material to crack due to lack of uniform expansion or contraction.

In contrast, increased densification typically requires slower, more controlled heating to allow for proper material structure formation. Running of the material generally involves the molten material moving out of place, which is not a consequence of rapid burning but rather improper handling or design. Evaporation of components may occur if materials are burned out too quickly, but this is secondary to the more observable cracking, which results from thermal shock. Thus, the most critical and immediate consequence seen with rapid burnout is the development of cracks in the investment material.